Effect of Porosity on Compressive Strength of Resin Modified Glass Ionomer Luting Cements
DOI:
https://doi.org/10.31436/imjm.v17i2.269Abstract
Introduction: The purpose of this study was to decide on the relation between types of mixing and the porosity of diameter (1-100) µm and compressive strength of RMGIC. Methods: Fifteen specimens 6mm height and 4mm in diameter were prepared for each type of luting cement and were stored in distilled water at 37° C for 24 hours. The compressive strength was determined. The fractured surfaces of 10 randomly selected specimens of each cement type were analyzed using SEM at 250 times magnification, and five photomicrographs were taken at five random places. All the photomicrographs were analyzed using image analyzer software to determine the amount and size of porosity present. Results: There was no significant difference in compressive strength between different mixing methods, but it had a significant impact by increasing the percentage of porosity of diameter (1-100) µm in diameter of RMGIC. There was no linear relationship between compressive strength and porosity (1-100) µm in diameter for both types of luting cements (P>0.05). Conclusion: No significant differences in compressive strength were found using different mixing methods. The size and number of porosity in the specimens of encapsulated cements were greater than those of hand-mixed cements. The porosity (1-100) µm in diameter and the compressive strength bore no linear relationship to each other.
Downloads
Downloads
Published
How to Cite
Issue
Section
License
All material submitted for publication is assumed to be submitted exclusively to the IIUM Medical Journal Malaysia (IMJM) unless the contrary is stated. Manuscript decisions are based on a double-blinded peer review process. The Editor retains the right to determine the style and if necessary, edit and shorten any material accepted for publication.
IMJM retain copyright to all the articles published in the journal. All final ‘proof’ submissions must be accompanied by a completed Copyright Assignment Form, duly signed by all authors. The author(s) or copyright owner(s) irrevocably grant(s) to any third party, in advance and in perpetuity, the right to use, reproduce or disseminate the research article in its entirety or in part, in any format or medium, provided that no substantive errors are introduced in the process, proper attribution of authorship and correct citation details are given, and that the bibliographic details are not changed. If the article is reproduced or disseminated in part, this must be clearly and unequivocally indicated.